Preparing 250 Tons of 8 Mm Copper Bars Tender, Iraq - 95921748

MINISTRY OF INDUSTRY AND MINERALS has floated a tender for Preparing 250 Tons of 8 Mm Copper Bars. The project location is Iraq and the tender is closing on 26 Feb 2024. The tender notice number is , while the TOT Ref Number is 95921748. Bidders can have further information about the Tender and can request the complete Tender document by Registering on the site.

Procurement Summary

Country : Iraq

Summary : Preparing 250 Tons of 8 Mm Copper Bars

Deadline : 26 Feb 2024

Other Information

Notice Type : Tender

TOT Ref.No.: 95921748

Document Ref. No. :

Competition : ICB

Financier : Self Financed

Purchaser Ownership : Public

Tender Value : Refer Document

Purchaser's Detail

Purchaser : MINISTRY OF INDUSTRY AND MINERALS
P.O BOX; 44 Nassiriyah Tel: +964- 234008)(234126-234128)8863705 Telefax: +964-1-8853077/ 42-230231
Iraq
Email :ur1.comp@industry.gov.iq/ ur.comp@industry.gov.iq/urscoe@yahoo.com

Tender Details

Tenders are invited for Preparing 250 Tons of 8 Mm Copper Bars

Supply of Copper Rod
Specification:
1. Nominal Diameter (8) Mm. Deviation Acc. To Astm B 49 .
2. Copper Content of the Rod - Min. 99.97 Percent .(Acc. To Din
1787-Astm-b49 Chemical Composition ).
3. Oxygen Content from 0.005 to 0.040 Percent, as for E-Cu 58 Acc .
To
Din 1787 (Used for Enameled Wire Production .the Type of Copper
Is
Etp (Electrolytic Tough Pitch Copper)).
4. Elongation at Break in Annealed Condition-Min. 35 Percent in 200
Mm Sample at a Speed Max. 300 Mm /Min.
5. Conductivity in Annealed Condition at 20 ˚C-Min. 58 M/ω
mm2 and
Conductivity Iacs at 20
°
C =101%.
6. Surface - Clean, Sound, Smooth, Free of Oxide, Pepes, Laps,
Cracks,
Kinks, Twists, Seams, Damaged Ends and Other Imperfections.
7. Delivery Mode- Coils Protected from Direct Sun Light, Packed for
Shipping acc.to Astm b49 Coil Weight shall be 3.5 Tons +5% .